There is a saying that adding silicon into aluminum alloy die casting mould can improve the application of alloy fluidity. In fact, this statement is not comprehensive, but there are misleading deviations. Next, Shandong Aluminum alloy die casting to understand the main purpose of adding silicon.
1. Adding silicon can increase the fluidity. This function is mainly used for gravity casting, such as filling under low pressure. In fact, there is not much difference between the alloy with or without silicon at the filling pressure of more than 1MPa. In today's casting process, the filling pressure can be greater than 100 MPa, the fluidity is poor, and there is no problem of insufficient alloy filling.
2、可以减少“液 - 固”相转变的体积收缩，来确定基于几个实验中，硅的约20％的铝的量，可以实现在相变的体积几乎没有变化。因此，如果是使用在进行高温工作场合的铝活塞，一般来说会是含硅比较具有较高的合金。由于在铸造工艺的特性的性质，高压填充在一个方向铸造金属，不具有反向进给的功能，这是它的低压铸造，重力铸造具有反向馈送的填充处理特性完全不同的地方。正是因为这个问题原因，行业上才特意配制相变收缩率比较低，含硅量尽量高，专门人员为了提高压铸工艺技术不能通过反向补缩。
2. The volume shrinkage of the "liquid-solid" phase transition can be reduced to determine that based on several experiments, the amount of about 20% aluminum in silicon can be achieved with almost no change in the volume of phase transformation. Therefore, if it is used in high-temperature working occasions of aluminum piston, generally speaking, it will have higher alloy containing silicon. Due to the characteristics of the casting process, high-pressure filling can cast metal in one direction without the function of reverse feeding. This is the filling treatment characteristics of low-pressure casting and gravity casting with reverse feeding. It is precisely because of this problem that the industry specially formulated phase transformation shrinkage rate is relatively low, silicon content is as high as possible, professionals in order to improve the die casting process technology can not pass the reverse feeding.
Adding silicon into the alloy has some disadvantages. At the same time, we also have some disadvantages. The cost is that the strength of the traditional alloy is greatly reduced, and the system is more fragile, and its elongation is also significantly reduced.
The above is the introduction of "is it necessary to add silicon in Shandong Aluminum alloy die casting die?" I hope to help you. If you want to know more, please pay attention to our website.